文献：

Multi-mode biodegradable tumourmicroenvironment sensitive nanoparticles for targeted breast cancer imaging

文献链接：

作者：

Zhenhui Nie, Ningbin Luo, Junjie Liu, Xinyi Zeng, Yu Zhang and Danke Su

相关产品：

Fe3O4 nanoparticles（四氧化三铁纳米颗粒）

Na2CO3（碳酸钠）

原文摘要：

Gas-filled ultrasound (US) contrast agents easily collapse in the body, and the gas can easily overflow, which limits the effectiveness of US imaging. To address this issue, an injectable gas-generating multi-mode system was developed that carries the MR negative contrast agent Fe3O4, the fluorescent dye Cy5.5, and the CO2 releasing donor (Na2CO3). The nanoparticles can continuously generate carbon dioxide (CO2) gas in acidic tumour tissue in the body, giving the tumour a strong echo signal under ultrasonic imaging. In addition, the nanoparticles confer excellent effects for MR and fluorescence imaging of the tumour tissue. The results indicate that this pH-responsive NP system provides good effects in MR/US/fluorescent imaging. This study provides a useful reference for multimode tumour imaging.

Fe3O4 nanoparticles （四氧化三铁纳米颗粒）是纳米级别的四氧化三铁材料。四氧化三铁也被称为磁性氧化铁，其晶体结构属于反尖晶石结构。在这个结构中，氧离子呈立方最密堆积，而铁离子则填充在氧离子构成的四面体和八面体空隙中。从化学组成上看，可以看作是，其中包含二价铁和三价铁，这使得它具有特殊的磁性。它的光学性质也很特殊。Na2CO3是碳酸钠的化学式，它由钠离子和碳酸根离子组成。碳酸钠也被称为纯碱、苏打。该文献基于Fe3O4 nanoparticles、Na2CO3的相关性质，Fe3O4/Na2CO3@PLGA/Cy5.5/cRGD纳米颗粒的合成如下：

图：合成流程

Fe3O4/Na2CO3@PLGA/Cy5.5/cRGD纳米颗粒的合成：

首先将PLGA和氯仿混合在一起。然后，依次加入 Cy5.5,油酸改性磁性纳米颗粒（OA@Fe3O4），碳酸钠（碳酸钠）和 PVA溶液，用超声波处理器乳化。然后，加入PVA溶液，室温搅拌，加入PVA溶液，搅拌过夜，去除残留的有机溶剂。上述溶液用ddH2O进行多次超滤洗涤，然后用PB缓冲液稀释。然后，在上述混合溶液中加入EDC和NHS。搅拌然后用超滤洗涤，并在PB缓冲溶液中重悬。然后，加入cRGD 搅拌过夜。为了去除EDC、NHS和任何残留的cRGD，透明溶液用超滤管过滤。最后，将Fe3O4/Na2CO3@PLGA/Cy5.5/cRGD NPs在去离子水中重悬，并在4°C下保存。

图：作用机制

结论：

该文献成功制备了基于Fe3O4 nanoparticles、Na2CO3 合成的Fe3O4/Na2CO3@PLGA/Cy5.5/cRGD纳米颗粒。实验证明，Fe3O4/Na2CO3@PLGA/Cy5.5/cRGD纳米颗粒对tumour组织的Mr和荧光成像具有良好的效果。此外，该纳米颗粒ph响应型NP系统在Mr/US/荧光成像中具有良好的效果。